Copper-tin-oxygen alloy plating

ABSTRACT

The present invention relates to a Cu—Sn—O alloy plating having an oxygen content of 0.3 to 50 at %, a copper content of 20 to 80 at %, and a tin content of 10 to 70 at % in the plating. The present invention provides a copper tin alloy plating that has excellent plating adhesion and disengaging force stability and particularly a Cu—Sn—O alloy plating that has a blackish color tone without containing any controlled substances.

TECHNICAL FIELD

The present invention relates to a copper-tin alloy plating used onornamental articles for use in clothing, such as broaches, buttons,buckles, fasteners and cuff buttons, accessories such as a necklace oran earring, toys, and other industrial goods. More particularly, thepresent invention relates to a copper-tin-oxygen alloy plating(hereinafter, referred to as Cu—Sn—O alloy plating) that has excellentplating adhesion and excellent disengaging power stability describedhereinbelow and has a black or black-based color without containing anycontrolled substances.

BACKGROUND ART

Clothing manufacturers are concerned about the danger that needles usedfor sewing clothes, bags, pouches, etc., if they are left to remain inthe products, could prick the human body and to prevent such danger,magnetic inspection for detecting needles has been conducted.Accordingly, nonmagnetic plating, for example, nickel-phosphorus platingor nickel-tin alloy plating has been predominantly used for ornamentalarticles for clothing. However, in recent years, it has been pointed outthat if nickel-containing metal contacts a human body, it can be anallergen to cause skin rashes or inflammation. Several countries in theworld, such as European countries and the United States of America, aregoing to take some measures (legislation) for protecting the human bodyfrom such a nickel allergy.

Under the circumstances, copper-tin alloy plating has been reviewed inrecent years as promising metal plating that substitutes for nickelalloy plating.

Many techniques have hitherto been proposed for copper-tin alloy platingas disclosed in JP 10-102278 A, JP 2001-295092A (U.S. Pat. No.6,416,571), etc. However, the conventional techniques have a problem ofinstability of a disengaging force. That is, when the conventionaltechnique is applied to ornamental articles like snap buttons, which areattached to clothes and repeatedly subject to resilient snap engagement,fluctuation of the disengaging force (i.e. force required fordisengaging a snap engagement) becomes greater as engagement anddisengagement are repeated, and eventually the disengaging force will beoutside of a specific range. As a result, when the disengaging force istoo strong, the cloth will be ruptured and on the contrary when thedisengaging force is too weak, the button will be disengaged of itself.Note that as shown in FIG. 1, which is a cross-sectional view showing asnap button, the snap button includes snaps used as a set, i.e., a malesnap 1 consisting of a stud member 3 having a round head 3 a that has agenerally extended (flared) top and a fitting member 4 for fitting thestud member 3 to a cloth 7, and a female snap 2 having a socket member 5resiliently engageable with the round head 3 a of the male snap 1 and afitting member 6 for fitting the socket member 5 to another cloth 8.

Further, when copper-tin alloy plating is applied to clothing ornaments,accessories or the like, the appearance color (color tone) of theplating is considered to be one of the important qualities required. Inthe copper-tin alloy plating, those platings having a red, yellow(gold), white, or silver white color tone have been realized by varyingthe contents of copper and of tin in the plating and on the other handthose platings having a black-based color tone have been realized byincorporating cobalt or selenium in the copper-tin plating.

However, since the use amounts of cobalt and selenium in thecopper-tin-(cobalt or selenium) alloy in the plating having ablack-based color tone are regulated by European Toy Safety StandardEN71-3 or Ecotex Standard 100, copper-tin alloy plating having ablack-based color tone without containing any such controlled substanceshas been demanded.

As far as is known, there has been made only one proposal for thecopper-tin alloy plating having a black-based color tone containing nosuch prohibited substance. That is, JP 10-102278 A discloses a method ofproducing copper-tin alloy plating having a pale black color tone with aCu/Sn weight ratio=41/59. The black plating taught in the document haspoor disengaging force stability and poor adhesion. As a result, aproblem arises, for example, that the plating migrates to the clothes byfriction with the clothes, so that the commercial value of the clothesis deteriorated, which prevents commercialization of the above-mentionedpale black copper-tin alloy plating.

Further, industrially operative plating having a black-based color tonefor ornamentation and corrosion resistance includes nickel-tin alloy.However, the plating has poor adhesion so that its disengaging forcestability is poor and, further, it causes a problem of nickel allergy.

DISCLOSURE OF THE INVENTION

Therefore, an object of the present invention is to provide a copper-tinalloy plating having excellent plating adhesion and excellentdisengaging force stability and more particularly a Cu—Sn—O alloyplating having a black-based appearance without containing anycontrolled substances.

The present inventors have made extensive studies on the compositions ofplating and qualities (the disengagement stability, plating adhesion,corrosion resistance, and color tone of plating) of copper-tin alloyplatings and as a result, they have found that incorporation of aspecified amount of oxygen in the plating to produce Cu—Sn—O alloyplating provides an alloy plating that not only has excellentdisengaging force stability without deteriorating plating adhesion andcorrosion resistance but also has a black-based color tone, therebyachieving the present invention.

That is, the present invention is composed of the following.

-   1. A Cu—Sn—O alloy plating having an oxygen content of 0.3 to 50 at    % in the plating.-   2. The Cu—Sn—O alloy plating as described in 1 above, wherein the    oxygen content is 0.5 to 47 at %.-   3. The Cu—Sn—O alloy plating as described in 1 above, wherein the    oxygen content is 1.5 to 50 at % and the plating has blackish    appearance.-   4. The Cu—Sn—O alloy plating as described in any one of 1 to 3    above, wherein a copper content is 20 to 80 at %, and a tin content    is 10 to 70 at % in the plating.

5. An ornamental article having Cu—Sn—O alloy plating as described inany one of 1 to 4 above.

6. The ornamental article as described in 5 above, wherein the articleis a snap button.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an explanatory cross-sectional view showing a snap button.

DETAILED DESCRIPTION OF THE INVENITON

Hereinafter, the present invention will be described in detail withreference to the attached drawing.

According to the present invention, it has been found that in order toachieve plating adhesion, corrosion resistance, and disengaging forcestability as desired, it is essential to adjust the content of oxygen inthe Cu—Sn—O alloy plating to 0.3 to 50 at %.

In the present invention, the means for incorporating oxygen into aplating is not particularly limited. A preferred method of incorporatingoxygen into a plating includes a method in which plating is performed ina plating bath containing, for example, an oxidizing agent and/or anadditive such as a special surfactant (for example, trade name: TopRinse, manufactured by Okuno Chemical Industry Co., Ltd.).

The reason why the incorporation of oxygen into a copper-tin alloyplating in a content of 0.3 to 50 at % improves disengaging forcestability of the plating is not clear. However, it may be presumed thatdue to oxides formed therein, (1) the hardness of the plating isincreased and (2) fine unevenness is formed on the surface of theplating to decrease a contact area of the portions where the male andfemale engagement members contact each other, thereby increasinglubricity and decreasing friction coefficient and other complex effects.Such complex effects may result in prevention of the occurrence ofgalling between the male and female members and/or reduction in abrasionof the plating.

If the oxygen content in the plating is less than 0.3 at %, the Cu—Sn—Oplating has an increased metallic property so that excellent disengagingforce stability as aimed at by the present invention cannot be obtained.On the other hand, if the oxygen content in the plating is above 50 at%, the Cu—Sn—O alloy plating is mostly constituted by oxides so that theplating adhesion becomes poor and also the disengaging force stabilityis decreased. To obtain particularly excellent disengaging forcestability and plating adhesion, it is preferred that the oxygen contentof the plating is within a range of 0.5 to 47 at % and more preferably1.0 to 37 at %.

Further, by containing the oxygen at a content of 1.5 at % or more, morepreferably 3 at % or more, and most preferably 5 at % or more, theplating can obtain a black-based appearance (blackish color). Only fromthe viewpoint of the color tone of the plating, an increased oxygencontent in the plating can lead to an increase in blackishness and hencethe oxygen content in the plating may be selected as appropriatedepending on the intended application. However, as described above,increasing the oxygen content in the plating excessively causes thedisengaging force stability and plating adhesion to become deteriorated.In the present invention, the oxygen content for providing a platinghaving a black-based color tone and excellent disengaging forcestability and plating adhesion of the plating is preferably 1.5 to 50 at%, more preferably 3 to 47 at %, and most preferably 5 to 37 at %.

Note that the black-based color tone referred to herein can be evaluatedby various methods. For example, it can be evaluated by the Hunterbrightness index (L value) (L=10×Y^(1/2)) (where Y is one of threestimulation values (variables) prescribed in JIS-Z-8722). Theblack-based color tone corresponds to one having an L value of 87 orless.

In the present invention, it is preferred that the copper content in theplating is within a range of 20 to 80 at % and the tin content in theplating is within a range of 10 to 70 at %. If the copper content in theplating is less than 20 at % or the tin content in the plating exceeds70 at %, the hardness of the plating is excessively decreased to providea plating having poor disengaging force stability. On the other hand, ifthe copper content in the plating exceeds 80 at % or the tin content inthe plating is less than 10 at %, the hardness of the plating becomesexcessively high so that the plating becomes brittle and both adhesionand corrosion resistance become poor.

Further, in the case of the copper-tin-oxygen alloy plating having ablack-based color tone, adjustment of the copper and tin contents in theplating achieves color variation, for example, reddish black, grayishblack, bluish black, greenish black, yellowish black or the like.

More preferred copper and tin contents are a copper content of 30 to 75at % and a tin content of 15 to 60 at %.

The Cu—Sn—O alloy plating of the present invention may containcomponents other than copper, tin and oxygen in small amounts so far asthey do not give adverse influences on the quality of the plating. Thatis, the Cu—Sn—O alloy plating of the present invention may containcomponents derived from raw material water for a plating solution, suchas calcium, silicon and chlorine and those components derived fromplating auxiliaries such as a brightener, for example, carbon, nitrogen,sulfur, phosphorus and the like in small amounts so far as suchcomponents do not adversely affect the quality of the platings.

In the present invention, the content ratio of copper, tin, and oxygenatoms are based on the results of compositional analysis in thedirection of the depth of the plating by an Auger electron spectroscopy(hereinafter referred to as the Auger method). However, the outermostsurface of the plating tends to fail to give exact analytical valueswith satisfactory reproducibility owing to effects such as naturaloxidation and surface contamination, so that the analytical valuesobtained on the outermost surface are excluded in the present invention.That is, those analytical values obtained on a portion that is lesssusceptible to natural oxidation, surface contamination and the like andalso to a change in the composition of the plating with time are adoptedas content values of copper, tin, and oxygen atoms. Usually, analyticalvalues of a portion at a depth of 10 nm or more (a value derived fromthe sputtering rate and sputtering time) from the outermost surfacetoward inside (toward the direction to substrate) are used.

According to one embodiment of the present invention, the Cu—Sn—O alloyplating of the present invention only needs to be applied onto asubstrate as an outermost plating layer and may be used either for asingle layer plated product or for a multilayer plated product.Specifically, it is possible to produce a plated product that includes asubstrate on which only one alloy plating of the present invention isapplied or a plated product that includes a substrate that has thereonalso at least one metal plating layer such as nickel plating, nickelalloy plating, copper plating, copper alloy plating, zinc plating, zincalloy plating, tin plating, tin alloy plating or the like as an underlayer below the Cu—Sn—O alloy plating so far as such does not harm thequality and performance of the plating. It is also possible to produce amultilayer plated product in which a plurality of plating layers of thesame Cu—Sn—O alloy are laminated on a substrate.

The substrate (article to be plated) that can be used in the presentinvention is not particularly limited and may be selected as appropriatedepending on the use. Examples of such a substrate include: metalmaterials such as iron, steel, copper, brass and the like copper alloys;ceramic materials or plastic materials; or articles made of ceramic orplastic materials on which some metal plating has been applied inadvance.

The thickness of the plating is not particularly limited and may beselected as appropriate depending on the intended use. It is desirablethat the thickness of the plating is 0.05 μm or more. If the thicknessof the plating is less than 0.05 μm, the quality and performance of theplating of the present invention cannot be obtained.

Further, the Cu—Sn—O alloy plating of the present invention may haveformed thereon a film of varnish or coating composition in order tofurther improve the design aesthetics and corrosion resistance of theplating.

As described above, in the Cu—Sn—O alloy plating of the presentinvention, a suitable amount of oxygen (0.3 to 50 at %) contained in theplating contributes to obtaining excellent plating adhesion, corrosionresistance and disengaging force stability. Further, adjusting theoxygen content to a specific range (1.5 to 50 at %) can provide aCu—Sn—O alloy plating having a black-based color tone.

The plated product of the present invention can be produced, forexample, by a method involving a conventional plating process using aplating bath having compounded therein the above-mentioned specialsurfactant component.

The process for producing plated products according to the presentinvention includes, for example, in the case of a single layer plating,degreasing treatment (immersion degreasing and/or electrolyticdegreasing)→rinsing with water→acid activation treatment→rinsing withwater→plating treatment→rinsing with water→drying (cf. Example 1described hereinbelow for details). Further, in the case of a two layerplating, the process includes degreasing treatment (immersion degreasingand/or electrolytic degreasing)→rinsing with water→acid activationtreatment→rinsing with water→plating treatment→rinsing with water→acidactivation treatment→rinsing with water→plating treatment→rinsing withwater→drying (cf. Examples 2 and 16 described hereinbelow for details),alternatively, the process includes degreasing treatment (immersiondegreasing and/or electrolytic degreasing)→rinsing with water→acidactivation treatment→rinsing with water→plating treatment→rinsing withwater→plating treatment→rinsing with water→drying (cf. Example 17described hereinbelow for details). However, the present invention isnot limited to the above-mentioned processes. For example,post-treatment step such as chemical forming treatment and coatingtreatment, baking step and the like during the plating process may becombined as appropriate or acid activation treatment, degreasingtreatment, rinsing with water or the like may be omitted or added asappropriate.

Examples of the means for performing plating treatment that can be usedin the present invention include known plating techniques such aselectroless plating and electroplating as typified by barrel plating,rack plating, and high speed plating.

The plating of the present invention can be used advantageously as aplating, particularly for ornamental articles for clothing as typifiedby buttons, buckles, slide fasteners, and cuff buttons, accessories suchas earrings and necklaces as well as toys and other industrial goods forproviding corrosion resistance or ornamentation thereto. However, thepresent invention is not limited thereto and can also be used forelectronic parts.

Since the Cu—Sn—O alloy plating of the present invention has excellentdisengaging force stability, it can be used preferably for use incostumery, in particular, as plating for snap buttons.

BEST MODE FOR CARRYING OUT THE INVENTION

Hereinafter, the present invention will be explained by examples andcomparative examples. However, the present invention should not beconsidered to be limited by the following description.

The copper content, tin content and oxygen content of a plated productin the examples and comparative examples were obtained by performinganalyses by an Auger electron spectroscopy in the depth direction underthe following measuring conditions and values after sputtering for 5minutes were adopted for analysis.

[Measuring Conditions]

-   Apparatus: PHI-660 (manufactured by Physical Electronics)    <Electron Beam Condition>

Accelerating voltage: 5 kV

Irradiation current: 0.5 μA

Measuring region: 200×200 μm²

<Ar⁺ Sputtering Condition>

Accelerating voltage: 3 kV

Sputtering region: 2×2 mm²

Sputtering speed: 11 nm/min (found value for SiO₂)

The appearance (color) of the plating was evaluated in the followingmanner. When the ornamental article in each of examples and comparativeexamples was placed in a barrel to carry out plating, simultaneously,one brass plate of 25 mm×25 mm was placed in a barrel to be plated, andL value of each plated brass was measured under the following conditions(note that the composition of the plating on the brass sample was thesame as the composition of the plating on the ornamental article platedin respective Example and Comparative Examples, and the appearance(color) was the same as well).

Apparatus: touch panel type SM Color Computer (Model SM-T), manufacturedby Suga Test Instruments Co., Ltd.

Measuring condition: Illuminant C, 2 degree standard observer angle,Measuring diameter: Φ 15 mm

Optical conditions: 8° illumination, receiving diffused light (8-Dmethod)

Evaluation standards are described below.

⊚: L value of less than 67

◯: L value of 67 or more and less than 77

Δ: L value of 77 or more and less than 87

x: L value of 87 or more.

[Plating Bath]

The plating solutions used in the Examples and Comparative Examples aredescribed below.

Plating Bath (1)

Potassium pyrophosphate: 300 g/l

Copper pyrophosphate: 0.6 g/l

Stannous pyrophosphate: 8 g/l

Methanesulfonic acid: 60 g/l

Glossing agent (reaction product of epichlorohydrin/anhydrouspiperazine=1 mol/l mol): 0.015 g/l (as an effective ingredient)

Perfluoroalkyltrimethylammonium salt: 0.003 ml/l

Surfactant (trade name: Top Rinse, manufactured by Okuno ChemicalIndustry Co., Ltd.): 1 ml/l

pH: 7.5

Plating Bath (2)

Potassium pyrophosphate: 300 g/l

Copper pyrophosphate: 0.6 g/l

Stannous pyrophosphate: 8 g/l

Methanesulfonic acid: 60 g/l

Glossing agent (reaction product of epichlorohydrin/anhydrouspiperazine=1 mol/l mol): 0.015 g/l (as an effective ingredient)

Perfluoroalkyltrimethylammonium salt: 0.05 ml/l

pH: 7.5

Plating Bath (3)

Stannous pyrophosphate: 23 g/l

Copper pyrophosphate: 7.5 g/l

Potassium pyrophosphate: 160 g/l

Glossing agent (reaction product of epichlorohydrin/anhydrouspiperazine=1 mol/1 mol): 4 ml/l (0.712 g/l as an effective ingredient)

Glossing auxiliary agent (Paraformaldehyde): 0.5 to 1.0 g/l

Surface tension treatment agent (Acetyleneglycol): 0.04 g/l

N-benzylnicotinium hydrochloride: 1 to 2 ml/l

p ratio (ration of ‘P₂O₇’ to ‘Sn+Cu’): 6.18

pH: 8.10

Plating Bath (4) (Commercially Available Tin Alkanesulfonate PlatingBath)

Ebasolder SN (based on organic acid and tin salt, manufactured byEbara-Udylite Co., Ltd.): 100 g/l (10 g/l as tin)

Ebasolder A (based on organic acid, manufactured by Ebara-Udylite Co.,Ltd.): 100 g/l

Ebasolder #10R (based on nonionic surfactant, cationic surfactant, andcarboxylic acid derivative, manufactured by Ebara-Udylite Co., Ltd.): 10ml/l

[Evaluation of Plating Composition, Plating Thickness, CorrosionResistance, Plating Adhesion, and Disengaging Force Stability of thePlated Ornamental Article]

Plating Thickness:

The cross-section of a plated product was observed on an electronmicroscope and the thickness of the plating was measured.

Corrosion Resistance:

Corrosion resistance was evaluated based on the degree of discolorationin appearance occurred after standing in a thermo-hygrostat at 60° C.and 98% RH for 20 hours.

◯: 5% or less of the surface area was discolored.

Δ: More than 5% and less than 25% of the surface area was discolored.

x: 25% or more of the surface area was discolored.

Plating Adhesion:

Test 1 (Transfer Test)

Samples were strongly rubbed against paper and presence or absence oftransfer of the plating on the paper was visually examined and evaluatedas follows.

-   -   ◯: Transfer was present.    -   x: Transfer was absent.

Test 2 (Pincers Peeling Test)

To more strictly evaluate plating adhesion, samples were crushed with apair of pincers in Test 2 and presence or absence of peeling of theplating at that time was visually evaluated by the following criteria.

-   -   ◯: No peeling of the plating was observed    -   x: Peeling of the plating was observed        Disengaging Force Stability:

After brass-made socket members (trade name: 16 Socket (manufactured byYKK Newmax Co., Ltd.)) were plated under the conditions as defined inthe respective Examples and Comparative Examples, the respective socketmembers were attached to individual cloths through fitting members.

Thereafter, engagement and disengagement of the snap buttons (socket andstud) having the same plating were repeatedly performed while measuringdisengaging force by a gauge for measuring tensile force each time. Thenumber of times of engagements performed when fluctuation band of thedisengaging force as compared with the first disengagement exceeds ±20%or more was defined as limit engagement time whereby the disengagingforce stability was evaluated (the greater the limit engagement time,the more excellent the disengaging force stability). Evaluationstandards are as follows.

⊚: 1,000 times or more

◯: 750 times or more and less than 1,000 times

Δ: 500 times or more and less than 750 times

x: Less than 500 times

EXAMPLE 1

15 kg of brass-made stud members (trade name: 16 Duo (manufactured byYKK Newmax Co., Ltd.)) were placed in a barrel and immersion degreasing(trade name: ACE CLEAN 5300 (manufactured by Okuno Chemical IndustriesCo., Ltd.): 60 g/l, 50° C., 12 minutes) and rinsing with water wereperformed. Thereafter, electrolytic degreasing (trade name: ACE CLEAN5300 (manufactured by Okuno Chemical Industries Co., Ltd.): 100 g/l, 50°C., 5 V, 12 minutes) and rinsing with water were further performed.Then, the stud members were immersed in a 3.5% hydrochloric acidsolution at room temperature for 6 minutes and rinsed with water, andbarrel plating was performed in the plating bath (1) at 30° C. at acurrent density of 0.15 A/dm² for 24 minutes. After, rinsing with water,the stud members were dried with hot air at 100° C. to obtain platedproducts of Example 1. The composition of plating, the thickness of theplating, corrosion resistance, adhesion of the plating, disengagingforce stability and color tone of the plated products were evaluated andTable 1 shows the results.

EXAMPLE 2

15 kg of brass-made stud members (trade name: 16 Duo (manufactured byYKK Newmax Co., Ltd.)) were placed in a barrel and immersion degreasing(trade name: ACE CLEAN 5300 (manufactured by Okuno Chemical IndustriesCo., Ltd.): 60 g/l, 50° C., 12 minutes) and rinsing with water wereperformed. Thereafter, electrolytic degreasing (trade name: ACE CLEAN5300 (manufactured by Okuno Chemical Industries Co., Ltd.): 100 g/l, 50°C., 5 V, 12 minutes) and rinsing with water were further performed.Then, the stud members were immersed in a 3.5% hydrochloric acidsolution at room temperature for 6 minutes and rinsed with water, andbarrel plating was performed in the plating bath (1) at 30° C. at acurrent density of 0.15 A/dm² for 24 minutes, and rinsing with water wasperformed. Further, after immersing the stud members again in the 3.5%hydrochloric acid solution at room temperature for 6 minutes, rinsingwith water was performed. Then, barrel plating was performed in theplating bath (1) at 30° C. at a current density of 0.15 A/dm² for 12minutes, and rinsing with water was performed. After that, the studmembers were dried with hot air at 100° C. to obtain plated products ofExample 2. The composition of plating, the thickness of the plating,corrosion resistance, adhesion of the plating, disengaging forcestability and color tone of the plated products were evaluated and Table1 shows the results.

EXAMPLE 3 to 15

In the same manner as in Example 1, 15 kg of brass-made stud members(trade name: 16 Duo (manufactured by YKK Newmax Co., Ltd.)) were placedin a barrel and pretreatments were preformed appropriately. Then, theplating bath (1) was adjusted for the concentrations of copperpyrophosphate, tin pyrophosphate, glossing agent and surfactant andbarrel plating was performed at varied current density at the time ofplating and varied plating time. After rinsing with water, the studmembers were dried with hot air at 100° C. to obtain plated products ofExamples 3 to 15 with different contents of copper, tin and oxygen inthe plating. The composition of plating, the thickness of the plating,corrosion resistance, adhesion of the plating, disengaging forcestability and color tone of the plated products were evaluated and Table1 shows the results.

EXAMPLE 16

15 kg of brass-made stud members (trade name: 16 Duo (manufactured byYKK Newmax Co., Ltd.)) were placed in a barrel and immersion degreasing(trade name: ACE CLEAN 5300 (manufactured by Okuno Chemical IndustriesCo., Ltd.): 60 g/l, 50° C., 12 minutes) and rinsing with water wereperformed. Thereafter, electrolytic degreasing (trade name: ACE CLEAN5300 (manufactured by Okuno Chemical Industries Co., Ltd.): 100 g/l, 50°C., 5 V, 12 minutes) and rinsing with water were further performed.Then, the stud members were immersed in a 3.5% hydrochloric acidsolution at room temperature for 6 minutes and rinsed with water, andbarrel plating was performed in the plating bath (2) at 30° C. at acurrent density of 0.15 A/dm² for 24 minutes, and rinsing with water wasperformed. Further, after immersing the stud members again in the 3.5%hydrochloric acid solution at room temperature for 6 minutes, rinsingwith water was performed. Then, barrel plating was performed in theplating bath (1) at 30° C. at a current density of 0.15 A/dm² for 12minutes, and rinsing with water was further performed. After that, thestud members were dried with hot air at 100° C. to obtain platedproducts of Example 16. The composition of plating, the thickness of theplating, corrosion resistance, adhesion of the plating, disengagingforce stability and color tone of the plated products were evaluated andTable 1 shows the results.

EXAMPLE 17

15 kg of brass-made stud members (trade name: 16 Duo (manufactured byYKK Newmax Co., Ltd.)) were placed in a barrel and immersion degreasing(trade name: ACE CLEAN 5300 (manufactured by Okuno Chemical IndustriesCo., Ltd.): 60 g/l, 50° C., 12 minutes) and rinsing with water wereperformed. Thereafter, electrolytic degreasing (trade name: ACE CLEAN5300 (manufactured by Okuno Chemical Industries Co., Ltd.): 100 g/l, 50°C., 5 V, 12 minutes) and rinsing with water were further performed.Then, the stud members were immersed in a 3.5% hydrochloric acidsolution at room temperature for 6 minutes and rinsed with water, andbarrel plating was performed in the plating bath (4) at 25° C. at acurrent density of 0.2 A/dm² for 20 minutes, and rinsing with water wasperformed. After that, barrel plating was performed in the plating bath(1) at 30° C. at a current density of 0.15 A/dm² for 12 minutes,followed by rinsing with water. Then, the stud members were dried withhot air at 100° C. to obtain plated products of Example 17. Thecomposition of plating, the thickness of the plating, corrosionresistance, adhesion of the plating, disengaging force stability andcolor tone of the plated products were evaluated and Table 1 shows theresults.

COMPARATIVE EXAMPLE 1

A plated product was obtained in the same manner as in Example 1 exceptthat the plating bath (2) was used to obtain a plated product ofComparative Example 1. The composition, the thickness of the plating,corrosion resistance, adhesion of the plating, disengaging forcestability and color tone of the plated products were evaluated and Table1 shows the results.

COMPARATIVE EXAMPLE 2

A plated product was obtained in the same manner as in Example 1 exceptthat the plating bath (3) was used under conditions of a bathtemperature of 50° C., a current density of 0.5 A/dm² and a plating timeof 20 minutes to obtain a plated product of Comparative Example 2(product equivalent to that of Example 4 of JP 10-102278A). Thecomposition of plating, the thickness of the plating, corrosionresistance, adhesion of the plating, disengaging force stability andcolor tone of the plated products were evaluated and Table 1 shows theresults.

COMPARATIVE EXAMPLE 3

15 kg of brass-made stud members (trade name: 16 Duo (manufactured byYKK Newmax Co., Ltd.)) were placed in a barrel and immersion degreasing(trade name: ACE CLEAN 5300 (manufactured by Okuno Chemical IndustriesCo., Ltd.): 60 g/l, 50° C., 12 minutes) and rinsing with water wereperformed. Thereafter, electrolytic degreasing (trade name: ACE CLEAN5300 (manufactured by Okuno Chemical Industries Co., Ltd.): 100 g/l, 50°C., 5 V, 12 minutes) and rinsing with water were further performed.Then, the stud members were immersed in a 3.5% hydrochloric acidsolution at room temperature for 6 minutes and rinsed with water.Thereafter, barrel plating was performed in the plating bath (1) at 30°C. at a current density of 0.15 A/dm² for 36 minutes, and rinsing withwater was performed. Further, after immersing the stud members in anEbonol C special (manufactured by Meltex Inc., 100° C.) solution for 1minute, followed by rinsing with water, they were dried with hot air at100° C. to obtain plated products of Comparative Example 3. Thecomposition of plating, the thickness of the plating, corrosionresistance, adhesion of the plating, disengaging force stability andcolor tone of the plated products were evaluated and Table 1 shows theresults.

TABLE 1 Composition of plating and quality and performance of platedproduct Composition of plating Adhesion of Disengaging Color OxygenCopper Tin Thickness of the Corrosion the plating force tone No. (at %)(at %) (at %) plating (μm) resistance Test 1 Test 2 stability L valueExample 1 12 70 18 0.19 ◯ ◯ ◯ ⊚ ⊚ 2 12 70 18 0.32 ◯ ◯ ◯ ⊚ ⊚ 3 13 42 450.22 ◯ ◯ ◯ ⊚ ⊚ 4 19 22 59 0.19 ◯ ◯ ◯ ◯ ⊚ 5 7 31 62 0.24 ◯ ◯ ◯ ◯ ⊚ 6 1870 12 0.21 Δ ◯ ◯ ⊚ ⊚ 7 6 78 16 0.21 Δ ◯ ◯ ⊚ ⊚ 8 4 63 33 0.32 ◯ ◯ ◯ ◯ ◯ 92 72 26 0.43 ◯ ◯ ◯ Δ Δ 10 28 56 16 0.95 ◯ ◯ ◯ ⊚ ⊚ 11 48 36 16 0.43 ◯ ◯ xΔ ⊚ 12 12 70 18 10.1 ◯ ◯ ◯ ⊚ ⊚ 13 40 40 20 0.5 ◯ ◯ ◯ ◯ ⊚ 14 27 45 28 1.2◯ ◯ ◯ ⊚ ⊚ 15 34 43 23 1.1 ◯ ◯ ◯ ⊚ ⊚ 16 12 70 18 1.3 ◯ ◯ ◯ ⊚ ⊚ 17 12 7018 3.1 ◯ ◯ ◯ ⊚ ⊚ Comparative 1 0 70 30 0.75 ◯ ◯ ◯ x x Example 2 0 41 590.23 Δ x x x Δ 3 53 31 16 0.21 x x x Δ ⊚

INDUSTRIAL APPLICABILITY

According to the present invention, plating that is (1) nonmagnetic, (2)free of causing metal allergy and (3) excellent in quality andperformances such as plating adhesion, disengaging force stability, andcorrosion resistance can be obtained. Further, plating that (4) has ablackish color tone without containing any controlled substances can beobtained.

1. An ornamental article having Cu—Sn—O alloy plating having an oxygencontent of 0.3 to 50 at % in the plating, wherein said plating isapplied to said ornamental article and said ornamental article is madefrom material selected from a group consisting of metal materials,ceramic materials, plastic materials, or ceramic or plastic materials onwhich a metal plating has been applied in advance, wherein saidornamental article is a costumery article or a toy.
 2. The ornamentalarticle as claimed in claim 1, wherein the oxygen content is 0.5 to 47at %.
 3. The ornamental article as claimed in claim 1, wherein theoxygen content is 1.5 to 50 at % and the plating has blackishappearance.
 4. The ornamental article as claimed in claim 1, wherein acopper content is 20 to 80 at %, and a tin content is 10 to 70 at % inthe plating.
 5. The ornamental article as claimed in claim 2, wherein acopper content is 20 to 80 at %, and a tin content is 10 to 70 at % inthe plating.
 6. The ornamental article as claimed in claim 3, wherein acopper content is 20 to 80 at %, and a tin content is 10 to 70 at % inthe plating.
 7. The ornamental article as claimed in claim 2, whereinthe costumery article is a snap button.
 8. The ornamental article asclaimed in claim 3, wherein the costumery article is a snap button. 9.The ornamental article as claimed in claim 4, wherein the costumeryarticle is a snap button.
 10. The ornamental article as claimed in claim5, wherein the costumery article is a snap button.
 11. The ornamentalarticle according to claim 1, wherein the costumery article is anarticle for clothing or an accessory for said clothing.
 12. Theornamental article according to claim 11, wherein the costumery articlecomprises a button, a buckle, a slide fastener, a cuff button, or ajewelry article.
 13. An ornamental article having Cu—Sn—O alloy platinghaving an oxygen content of 0.3 to 50 at % in the plating, wherein saidplating is applied to said ornamental article and said ornamentalarticle is made from material selected from a group consisting of metalmaterials, ceramic materials, plastic materials, or ceramic or plasticmaterials on which a metal plating has been applied in advance, whereinsaid ornamental article is a snap button.